%0 Articles %T The effect of lignin content and lignin modification on Norway spruce wood properties and decay resistance %A Raiskila, Sanni %D 2008 %J Dissertationes Forestales %V 2008 %N 68 %R doi:10.14214/df.68 %U http://dissertationesforestales.fi/article/1851 %X Three different Norway spruce cutting clones growing in three environments with different soil and climatic conditions were studied. The purpose was to follow variation in the radial growth rate, wood properties and lignin content and to modify wood lignin with a natural monolignol, coniferyl alcohol, by making use of inherent wood peroxidases. In addition, the incorporation of chlorinated anilines into lignin was studied with synthetic model compounds and synthetic lignin preparations to show whether unnatural compounds originating from pesticides could be bound in the lignin polymer. The lignin content of heartwood, sapwood and earlywood was determined by applying Fourier transform infrared (FTIR) spectroscopy and a principal component regression (PCR) technique. Wood blocks were treated with coniferyl alcohol by using a vacuum impregnation method. The effect of impregnation was assessed by FTIR and by a fungal decay test. Trees from a fertile site showed the highest growth rate and sapwood lignin content and the lowest latewood proportion, weight density and modulus of rupture (MOR). Trees from a medium fertile site had the lowest growth rate and the highest latewood proportion, weight density, modulus of elasticity (MOE) and MOR. The most rapidly growing clone showed the lowest latewood proportion, weight density, MOE and MOR. The slowest growing clone had the lowest sapwood lignin content and the highest latewood proportion, weight density, MOE and MOR. Differences between the sites and clones were small, while fairly large variation was found between the individual trees and growing seasons. The cutting clones maintained clone-dependent wood properties in the different growing sites although variation between trees was high and climatic factors affected growth. The coniferyl alcohol impregnation increased the content of different lignin-type phenolic compounds in the wood as well as wood decay resistance against a white-rot fungus, Coriolus versicolor. During the synthetic lignin preparation 3,4-dichloroaniline became bound by a benzylamine bond to β-O-4 structures in the polymer and it could not be released by mild acid hydrolysis. The natural monolignol, coniferyl alcohol, and chlorinated anilines could be incorporated into the lignin polymer in vivo and in vitro, respectively.